Yttria Stabilized Zirconia Ceramic Rod

Yttria Stabilized Zirconia Ceramic Rod

1. Zirconia ceramic rod  has the highest strength and toughness at room temperature of all the advanced ceramic materials. The fine grain size allows for extremely smooth surfaces and sharp edges.

2. Excellent thermal insulation/low thermal conductivity (2.5 to 3 W/mK),

3. Very high resistance to crack propagation, high fracture toughness (6.5 to 8 MPam1/2).

Product NameZirconia Ceramic Rod / Small Ceramic Bar
Materialzirconia ceramic
Colorwhite or black ,blue or custom
Standardaccording the request of customer
precision 0.001mm
diameter 0.4-200mm
length 5-400mm
UsedRefractory Zirconia Ceramic Rod / Rod Ceramic High Hardness

Zirconia Ceramic Rod is the most widely applied and cost effective technical ceramic material. It offers a combination of superior mechanical strength and electrical properties, wear resistance and corrosion resistance. The maximum working temperature is up to 1700 °C with relatively high thermal conductivity. It is also an electrically insulating material with a high electrical resistivity. The good corrosion resistance makes it insoluble in water and slightly soluble in strong acid and alkaline solution.

 

Yttria Stabilized Zirconia Ceramic Rod
Material Properties:

95% Alumina99% AluminaZirconiaSilicon carbideSilicon nitrideAluminum nitrideMachinable ceramic
ColourwhiteLight yellowwhiteblackblackgraywhite
Density (g/cm3)3.7g/cm33.9g/cm36.02g/cm33.2g/cm33.25g/cm33.2g/cm32.48g/cm3
Water Absorption0 %0 %0 %0 %0 %0 %0 %
Hardness(HV)23.723.716.53320––
Flexural Strength(MPa)300MPa400MPa1100MPa450MPa800MPa310MPa91MPa
Compressive Strength(MPa)2500MPa2800MPa3600MPa2000MPa2600MPa–340MPa
Young’s Modulus Of Elasticity300GPa300GPa320GPa450GPa290GPa310~350GPa65GPa
Poisson’s Ratio0.230.230.250.140.240.240.29
Thermal Conductivity20W/m°C32W/m°C3W/m°C50W/m°C25W/m°C150W/m°C
1.46W/m°C
Dielectric Strength14KV/mm14KV/mm14KV/mm14KV/mm14KV/mm14KV/mm14KV/mm
Volume Resistivity(25ºC)>1014Ω·cm>1014Ω·cm>1014Ω·cm>105Ω·cm>1014Ω·cm>1014Ω·cm>1014Ω·cm
This data is typical for laboratory testing and the actual characteristics of a particular production batch may vary.

Machining Accuracy

(1) Axis: roundness 0.002 mm, concentricity 0.002 mm, smoothness Ra0.1;
(2) Hole: the minimum processing hole diameter is 0.2 mm and the depth is up to 6 mm (depending on the material);
(3) Slot (seam): a minimum of 0.1 mm narrow groove, and grooves of various shapes;
(4) Plane: 0.1MM sheet with minimum processable thickness, parallelism 0.001mm, measurement tolerance 0.001 mm, finish Ra0.1;